性能

key.properties.Title

Density 0.93 g/cm3
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 0.35

app.properties.Title

Anti-block No
Slip No

typical.properties.Title

Dart Drop Impact (ASTM D1709A) in grams (lbs) 130
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 110
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 610
Fabrication Method Blown Film Extrusion, Cast Film Extrusion
Functionality Mechanical Performance
Gloss (45 degree) 28
Haze (ASTM D1003) 36 %
Melting Point, DSC (Dow Method) in °C(°F) 121 (250)
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) 2.44 (29.5)
Tensile Elongation at Break, MD 150 %
Tensile Elongation at Break, TD 580 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 18.0 (2610)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 18.6 (2700)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 10.6 (1540)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 10.5 (1520)
Vicat Softening Point in °C(°F) 99.5 (211)